The electrorefining experiments with an anode composed of U, Y, Gd, Nd and Ce were carried out in the KCl-LiCl and LiF-NaF-KF(FLINAK) eutectic melt at 500 ℃ and 600 ℃, respectively. Uranium was the major component in the cathode deposits, and the separation factors of uranium with respect to the rare earths (REs) were nearly same in both electrolytes. REs concentrations in the molten salts and cathode deposits increased sharply at above 1.9 V, which was the decomposition voltage of REs. The current efficiency was inversely proportional to the applied voltage in the range of 1.0 V to 1.9 V (vs. STS304 and Ni).