초록 close

고상반응법으로 SrCl2:Eu2+ 형광체를 제작하고, 제작한 형광체의 광자극발광과 광발광 특성을 조사하였다. SrCl2:Eu2+ 형광체의 광발광 및 광자극발광은 Eu2+의 5d→4f 천이에 기인되었으며, 355 nm의 광으로 여기시켰을 때 광자극발광과 광발광 스펙트럼의 파장범위는 모두 380∼440 nm 이었고, 피이크 파장은 407 nm 이었다. SrCl2:Eu2+ 형광체의 선량의존성은 2.5 mGy∼200 mGy 영역에서 우수한 선형성을 나타내었으며, 상온에서 광자극발광의 fading은 20 분에 60%이었다.


SrCl2:Eu2+ phosphors were prepared by the solid phase reaction method, and their photostimulated luminescence(PSL) and photoluminescence(PL) characteristics were investigated. The PSL and PL peak of the SrCl2:Eu2+ phosphors are due to the 5d → 4f transition of Eu2+ ions in phosphors. The PSL and PL spectrum obtained by the 355 nm excitation was observed in 380∼440 nm region with the peak at 407 nm. The dose response of the PSL phosphors were linear within 2.5 mGy ∼ 200 mGy of 100 kV X-ray. The fading of the phosphors at room temperature was approximately 60% after 20 min.